纖維水泥平板 fiber cement flat sheets
以水泥為膠凝材料，有機(jī)合成纖維、無(wú)機(jī)礦物纖維或纖維素纖維等為增強(qiáng)材料，經(jīng)成型、加壓(或非加壓)、蒸壓(或非蒸壓)養(yǎng)護(hù)制成的板材。A plate made of cement as cementitious material, organic synthetic fiber, inorganic mineral fiber or cellulose fiber as reinforcing material, and cured by molding, pressurization (or non-pressurization) , autoclaving (or non-autoclaving)

無(wú)石棉纖維水泥平板 non-asbestos cement flat sheets用非石棉類纖維作為增強(qiáng)材料制成的纖維水泥平板。A fiber-cement plate made of non-asbestos fibers as a reinforcing material.

工業(yè)涂裝及貼面用纖維水泥板 fiber cement flat sheets for industrial coatings and veneering可用于工業(yè)化涂裝工藝或貼面工藝生產(chǎn)的無(wú)石棉纖維水泥平板。A fiber-cement plate made of non-asbestos fibers as a reinforcing material.

物理性能

（1）表觀密度/ (g/cm)不小于制造商文件中標(biāo)明的規(guī)定值      （2）導(dǎo)熱系數(shù)/[W/(m·K)  A類≤0.45 B類≤0.35 C類≤0.25 （3）含水率/% A類≤10  B類≤11 C類≤12

（4）吸水率/% A類≤25 B類≤30  C類≤40                            （5）濕脹率/%DS板≤0.2 PS板≤0.4                               （6）放射性 放射性內(nèi)照射指數(shù)IRA≤1.0外照射指數(shù)Iy≤1.0
 

 (7)不透水性  GB 8624-2012不燃性A級(jí)                                 (8)24h 檢驗(yàn)后板的底面允許出現(xiàn)潮濕的痕跡，但不應(yīng)出現(xiàn)水滴.

(9)抗凍性試驗(yàn) 經(jīng)100 次凍融循環(huán)，不得出現(xiàn)破裂、分層,經(jīng)50次凍融循環(huán)不得出現(xiàn)破裂、分層.抗折強(qiáng)度比率≥70%

（10）熱雨試驗(yàn)經(jīng)50 次循環(huán)試驗(yàn)不得開裂分層。                   (11)熱水試驗(yàn)  抗折強(qiáng)度比率>60%

(12)浸泡-干燥試驗(yàn)抗折強(qiáng)度比率≥70%

、
注1:夏熱冬暖地區(qū)可不做抗凍性。

注2: 抗陳性試驗(yàn)、熱水試驗(yàn)、浸泡-干燥試驗(yàn)進(jìn)行抗折強(qiáng)度比率試驗(yàn)時(shí)，試驗(yàn)試件及對(duì)比試件均為飽水狀態(tài)

A類板應(yīng)用于嚴(yán)寒地區(qū)時(shí)，抗凍性試驗(yàn)溫度條件調(diào)整為 -40C~20C。